Mechanical and Optical Characterization of Single-shade Resin Composites Used in Posterior Teeth.

OBJECTIVES: This study aimed to evaluate the optical and mechanical performance of two single-shade resin-based composites (RBCs) compared to those of a conventional RBC for restoring posterior teeth. METHODS: Two single-shade RBCs, Omnichroma (Tukoyama) and Vittra Unique APS (FGM), and a conventional RBC, Filtek Z350XT shade A2 (3M Oral Care), were evaluated in this study. The optical shade-matching performance was measured using a spectrophotometer. The light emitted by VALO Grand (Ultradent) and transmitted through the 2.0-mm RBC specimens was evaluated using beam profiling. Knoop hardness (KH, N/mm2), degree of conversion (DC, %) at the top and bottom, flexural strength (FS, MPa), elastic modulus (E, GPa), postgel shrinkage (Shr, %), and shrinkage stress (MPa) were evaluated. Scanning electron microscopy (SEM) was used to characterize the filler. Data for FS, E, and Shr were analyzed by one-way analysis of variance (ANOVA) and KH and DC by repeated one-way ANOVA measurement followed by Tukey test (α=0.05). The modified von Mises stress values, light transmission, and SEM images were analyzed qualitatively. RESULTS: All single-shade RBCs exhibited higher chromatic adaptation than the Filtek Z350XT (p<0.001). Omnichroma exhibited less color difference than Vittra Unique APS, irrespective of the shade. The light transmitted through Omnichroma and Vittra Unique APS increased during polymerization. KH and DC values were significantly reduced from the top to the bottom of the specimens for all RBCs (p<0.001); however, the ratio values were always higher than 80%. In general, all RBCs demonstrated similar mechanical properties. All RBCs exhibited a similar FS (p=0.083) and Shr value (p=0.144). Filtek Z350XT exhibited significantly higher E (p<0.001) than both single-shade RBCs. All RBCs exhibited similar shrinkage stress during restoration and similar residual stress during occlusal loading. CONCLUSIONS: Single-shade Omnichroma and Vittra Unique APS increased light transmission during light-activation, demonstrating better chromatic adaptation than conventional Filtek Z350XT. In general, Omnichroma and Vittra Unique APS exhibited similar mechanical properties and shrinkage stress distributions as Filtek Z350XT during light-activation and occlusal loading.

Effect of Activated Charcoal Toothpaste on Color Stability of Bleached Teeth Immersed in Different Drinks.

OBJECTIVE: This study aimed to evaluate the effect of activated charcoal toothpaste on the color stability of teeth subjected to tooth bleaching and pigmenting agents. METHODS: A total of 120 bovine crowns were randomly divided into 12 groups (n=10) according to two study factors: staining solutions (three levels): saliva (control), coffee, and red wine; and toothpaste (four levels): BPC, Bianco Pro Clinical (Bianco Oral Care) (Control); BIW, Black is White (Curaprox); BCA, Bianco Carbon (Bianco Oral Care); and NAT, Natural Suavetex (Suavetex). The samples were subjected to office bleaching with a 35% hydrogen peroxide-based gel (Whiteness HP Blue, FGM), followed by immersion in the solution for 45 minutes per day and daily toothbrushing for 7 days. The color (ΔE) and luminosity changes (ΔL*) were measured using reflectance spectroscopy (Vita EasyShade). The CIE values (L*, a*, b*) were measured at baseline after bleaching (T0) and immediately after immersion in solution each day (Ti1-Ti7) and after all toothbrushing cycles (Tb1-Tb7). ΔE and ΔL were analyzed using a two-way analysis of variance and Tukey's test (α=0.05). The clinically unacceptable level of ΔE > 3.3 was used to evaluate the color change. RESULTS: The color change was significantly influenced by the staining solutions and toothpastes (p<0.001). The color change (ΔE) was significantly higher when immersed in wine than in coffee, and lower ΔE values were observed for artificial saliva (control), irrespective of the toothpaste used. In artificial saliva, BPC, BIW, and BCA resulted in significantly lower ΔE values than NAT, which presented a clinically unacceptable level of dental color change (ΔE>3.3). Coffee resulted in a lower (L*) reduction than wine, irrespective of the toothpaste used. CONCLUSION: Charcoal toothpastes resulted in a color change on the surface of the tooth enamel (ΔE). The bleaching effect of the charcoal toothpastes and control evaluated in this study partially reduced the color changes on the surface of the tooth enamel caused by staining solutions but was unable to reestablish the measured values to the baseline. For teeth immersed in artificial saliva, the color change was not noticeable in BCA, BIW, and control-BPC (ΔE≥3.3), except for NAT, which showed a significant color change.

Effects of Charcoal Toothpaste on the Surface Roughness, Color Stability, and Marginal Staining of Resin Composites.

OBJECTIVE: This study was designed to evaluate the effects of charcoal toothpaste on the surface roughness, color stability, and marginal staining of resin composite restorations. METHODS: A total of 100 bovine incisors was collected. The crowns were sectioned and randomly divided into 10 groups (n=10) according to two study factors: toothpaste groups and nanoparticle resin composite groups. Five toothpastes-Bianco Pro Clinical (Bianco Oral Care, Uberlândia, MG, Brazil) - Control group; Bianco Carbon (Bianco Oral Care); NAT, Natural Suavetex Carvão Ativado (Suavetex, Uberlândia, MG, Brazil); Nano Action Black Be Emotion (Polishop, Jundiaí, SP, Brazil); and BIW, Black is White (Curaprox, Curaden AG, Kriens, Switzerland)-and two resin composites-Z350XT (Filtek Z350XT, 3M Oral Care) and Vittra (Vittra APS FGM, Joinville, SC, Brazil)-were used. Circular cavities with a diameter of 4 mm and a depth of 1 mm were prepared on the buccal face of the tooth crowns and restored with resin composites. The specimens were subjected to three months of simulated toothbrushing. The surface roughness (right angle [Ra], in micrometers [µm]) of the resin composites was measured before and after toothbrushing in five areas per specimen. The resin composite color and luminosity changes (ΔE and ΔL, respectively) were measured using reflectance spectroscopy (Vita EasyShade). Macro photographs were taken before and after toothbrushing to qualitatively analyze the marginal staining (MSt) of the resin composite restorations. Scanning electron microscopy (SEM) was performed before and after the simulated toothbrushing. Ra data were analyzed using two-way analysis of variance with repeated measures and the Tukey HSD test; MSt was analyzed using Kruskal-Wallis and Dunn tests (α=0.05), and the resin composite color change was analyzed using the clinically unacceptable level of ΔE > 3.3. RESULTS: Simulated brushing increased Ra irrespective of the resin composite or toothpaste used. No significant differences were found in Ra between the control group and all groups on which the charcoal toothpastes were tested. A clinically unacceptable level of resin composite color change (ΔE>3.3) was found after the use of most charcoal toothpastes. Use of Bianco Carbon resulted in marginal staining similar to that of the control group and was lower than that of the other charcoal toothpastes. Vittra brushed with black toothpaste showed the highest marginal staining. CONCLUSION: Use of charcoal toothpaste resulted in Ra values of resin composites similar to those found with conventional toothpastes. Charcoal toothpaste generally resulted in clinical resin composite color changes (ΔE). All charcoal toothpastes, except Bianco Carbon, caused marginal staining of the resin composite restorations.

Post-gel and Total Shrinkage Stress of Conventional and Bulk-fill Resin Composites in Endodontically-treated Molars.

CLINICAL RELEVANCE: The clinician should consider the polymerization shrinkage stress when selecting a composite resin for posterior restorations. The use of post-gel shrinkage values should guide the selection of a composite resin for posterior teeth. SUMMARY: Objectives: The objective of this study was to evaluate the effect of the method used for calculation of polymerization shrinkage, total or post-gel, on the shrinkage stress of conventional and bulk-fill composite resins for restoring endodontically treated teeth using finite element analysis.Methods and Materials: Four composite resins were tested for post-gel shrinkage (P-Shr) by the strain-gauge test and total shrinkage (TShr) using an optical method (n=10). Two conventional composite resins, Filtek Z350 XT (3M-ESPE; Z350) and TPH3 Spectrum (Dents-ply; TPH3) and two bulk-fill composite resins. Filtek Bulk-Fill Posterior (3M-ESPE; POST) SureFil SDR flow (Dentsply; SDR) were tested. Elastic modulus (E), diametral tensile strength (DTS), and compressive strength (CS) were also determined (n=10). The residual shrinkage stress was evaluated by finite element analysis with four restorative techniques: incremental with Z350 and TPH3; SDR/TPH3 (two bulk increments of 4 mm and two occlusal increments); and two bulk increments of 5 mm for POST. Data for P-Shr, T-Shr, E, DTS, and CS were analyzed by analysis of variance and Tukey's test (α=0.05), and residual shrinkage was analyzed quantitatively and qualitatively by the modified von Mises criteria.Results: SDR had the lowest CS values, POST and TPH3 had similar and intermediate values, and Z350 had the highest CS. TPH3 and Z350 had similar DTS values and values higher than SDR. Z350 and POST had higher P-Shr, and SDR had lower T-Shr. T-Shr resulted in higher shrinkage stress than P-Shr values. SDR/TPH3 resulted in higher shrinkage stress when using T-Shr and lower values when using the P-Shr value.Conclusion: T-Shr resulted in higher stress in the enamel and in root dentin close to the pulp chamber than P-Shr values. The selection of the T-Shr or P-Shr changed the ranking of the shrinkage stress of the tested composite resin.

Mechanical properties, shrinkage stress, cuspal strain and fracture resistance of molars restored with bulk-fill composites and incremental filling technique.

OBJECTIVES: To compare bulk-fill with incremental filling techniques for restoring large mesio-occlusal-distal (MOD) restorations. METHODS: Seventy-five molars with MOD preparations were divided into five groups: Z350XT, incrementally filled with Filtek Z350XT and four bulk-fills-FBF/Z350XT, Filtek Bulk Fill/Filtek Z350XT; VBF/CHA, Venus Bulk Fill/Charisma Diamond; SDR/EST-X, SDR/Esthet-X HD; TEC, TetricEvoCeram Bulk Fill. Cuspal strains were measured using strain-gauges (n=10): CSt-Re, during restorative procedure; CSt-100N, during 100N occlusal loading; CSt-Fr, at fracture load. Before fracture load, teeth were load-cycled. Fracture resistance, fracture mode, and enamel cracks were recorded. The other five teeth were used for Elastic modulus (E) and Vickers hardness (VH). Post-gel shrinkage (Shr), diametral tensile strength (DTS) and compressive strength (CS) were determined (n=10). Shrinkage stresses were analyzed using finite element analysis. RESULTS: SDR had similar CS values as TEC, lower than all other composites. CHA had similar DTS values as Z350XT, higher than all other composites. Z350XT had the highest mean Shr and SDR the lowest Shr. New enamel cracks and propagation was observed after the restoration, regardless of filling technique. Z350XT had lower fracture resistance than bulk-fill composite techniques. No significant differences in failure modes were found. E and VH were constant through the depth for all techniques. Bulk-filling techniques had lower stresses compared to Z350XT. CONCLUSIONS: Flowable bulk-fill composites had lower mechanical properties than paste bulk-fill and conventional composites. All bulk-fill composites had lower post-gel shrinkage than conventional composite. Bulk-fill filling techniques resulted in lower cusp strain, shrinkage stress and higher fracture resistance. CLINICAL SIGNIFICANCE: Using bulk-fill composites cause lower CSt wich indicates lower stress in restored tooth. Furthermore, bulk-fill composites have a higher fracture resistance. Therefore, clinicians may choose the bulk-fill composite to decrease undesirable effects of restoration while simplifying filling procedure.